Abstract:
A new series of red phosphors based on Eu(3+)-doped yttrium cerate [Y1.9Ce2O7:0.1Eu(3+), Y2Ce1.9O7:0.1Eu(3+) and Y2Ce2-xO7:xEu(3+) (x = 0.05, 0.10, 0.15, 0.20, 0.25 and 0.50)] was prepared via a conventional solid-state method. The influence of the substitution of Eu(3+) at the aliovalent site on the photoluminescent properties was determined by powder X-ray diffraction, FT Raman spectroscopy, X-ray photoelectron spectroscopy, transmission electron microscopy, scanning electron microscopy with energy-dispersive spectroscopy, UV-visible absorption spectroscopy, photoluminescence spectroscopy and lifetime measurements. The substitution of Eu(3+) at the Ce(4+) site induces a structural transition from a defect fluorite to a C-type structure, which increases the oxygen vacancy ordering and the distortion of the Eu(3+) environment, and decreases the formation of Ce(3+) states. In contrast, phosphors with isovalent substitution at the Y(3+) site exhibit the biphasic nature of defect fluorite and a C-type structure, thereby increasing the number of Ce(3+) oxidation states. These modifications resulted in remarkable changes in the photoluminescent properties of Y2Ce1.9O7:0.1Eu(3+) red phosphors, with emission intensities 3.8 times greater than those of the Ce0.9O2:0.1Eu(3+) and Y1.9Ce2O7:0.1Eu(3+). The photoluminescent properties of Y2Ce2-xO7:xEu(3+) were studied at different Eu(3+) concentrations under excitation with blue light. These phosphors emit intense red light due to the (5)D0-(7)F2 transition under excitation at 466 nm and no concentration quenching is observed with up to 50 mol% Eu(3+). They show increased lifetimes in the range 0.62-0.72 ms at Eu(3+) concentrations. The cation ordering linked to the oxygen vacancy ordering led to the uniform distribution of Eu(3+) ions in the lattice, thus allowing higher doping concentrations without quenching and consequently increasing the lifetime of the (5)D0 states. Our results demonstrate that significant improvements in the photoluminescence properties can be achieved by the structural alteration of a fluorite CeO2 to a C-type lattice.