A new series of high near-infrared (NIR) reflecting pigments with colors ranging from yellow to red by tuning the
Bi2Ce2O7 with rare earth ion substitutions on both A and B sites were synthesized by a solid state reaction
method. The resulting colorants were evaluated for their structural and optical properties. The absorption edge is gradiently red shifted on substitution from Y to Tb resulting colors yellow to red. The XPS analysis surmises the presence of the elements with trends of reduction in Ce3+ concentration on both substitutions. These results suggest that the color shift is mainly due to charge transfer band shift of the O2− to Ce4+ (4f-5d) and deep red shift is due to the introduction of additional energy level by terbium ions. A brilliant yellow hue was obtained for Bi1.75Y0.25Ce2O7 (b∗=51.4), whereas Bi2Ce1.50Tb0.50O7 (a∗=15.0) exhibited a red color. High NIR solar reflectance of 93% and 88% were obtained for Bi0.5Y1.5Ce2O7 yellow and Bi2Ce1.50Tb0.50O7 red pigments respectively. The application study of these selected pigments was investigated in the polymer matrix which demonstrates their coloring performance for various potential applications. These results demonstrate the synthesized pigments as potential near infrared reflective candidates for cool roof applications.