Abstract:
Ambient pressure drying has been carried out for the synthesis of silica-titania aerogel monoliths. The prepared aerogels show densities in the range 0.34-0.38 g/cm(3). The surface area and pore volume of these mixed oxide aerogels are comparable to those of the supercritically dried ones. The surface area for 5wt% titania aerogel has been found to be as high as 685 m(2)/g with a pore volume of 2.34 cm(3)/g and the 10wt% titania aerogel has a surface area of 620 m(2)/g with a pore volume of 2.36 cm(3)/g. Some gels were also made hydrophobic by a surface treatment with methyltrimethoxysilane and trimethylchlorosilane. The surface modified aerogels possess high surface areas in the range of 540-640 m(2)/g, and are thermally stable in terms of retaining hydrophobicity up to a temperature of 520 A degrees C. The pore size distribution of the aerogels clearly indicates the preservation of the aerogel structure. High Resolution Transmission Electron microscopy has been employed to characterise the aerogels and Fourier Transform infrared spectroscopy to study the effect of titania addition to silica and the surface modification. X-ray diffraction patterns were recorded to verify the molecular homogeneity of the aerogel.